SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
SAE 316 stainless steel is a molybdenum-alloyed steel and the second most common austenitic stainless steel (after grade 304). It is the preferred steel for use in marine environments because of its greater resistance to pitting corrosion than most other grades of steel without molybdenum. [ 1 ]
The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels. These efforts were similar ...
SAE 316 and SAE 316L stainless steel, also referred to as marine grade stainless, is a chromium, nickel, molybdenum alloy of steel that exhibits relatively good strength and corrosion resistance. 316L is the low carbon version of 316 stainless steel. [2] 316L in particular is biocompatible when produced to ASTM F138 / F139. [3]
Many material or standard specifications include a number of different UNS numbers that may be used within that specification. For example: UNS S30400 (SAE 304, Cr/Ni 18/10, Euronorm 1.4301 stainless steel) could be used to make stainless steel bars ( ASTM A276 ) or stainless steel plates for pressure vessels ( ASTM A240 ) or pipes ( ASTM A312 ).
One popular stainless steel grade used in 3D printing is 316L stainless steel. Due to the high temperature gradient and fast rate of solidification, stainless steel products manufactured via 3D printing tend to have a more refined microstructure; this, in turn, results in better mechanical properties.
For more severe corrosion conditions, when 304 stainless steel is too sensitive to pitting or crevice corrosion by chlorides or general corrosion in acidic applications, it is commonly replaced by 316 stainless steel. 304 and 302 stainless steels are subject to chloride stress fracture failure when used in tropical salt water conditions such as ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.