The powder injection molding process Complex geometry in one component instead of an assembly of many items Eyeglass components produced by powder injection molding. In the monograph P.O. Gribovsky, published in 1956, describes in detail the technology of hot casting (hot molding) ceramic products under pressure (now, Low Pressure Powder Injection Molding) and, in particular, notes that "hot ...
Tube drawing is very similar to bar drawing, except the beginning stock is a tube. It is used to decrease the diameter, improve surface finish, and improve dimensional accuracy. A mandrel may or may not be used depending on the specific process used. A floating plug may also be inserted into the inside diameter of the tube to control the wall ...
Presently, CSST and FAC tubing both use corrugated stainless steel tubing. In the past, FAC used corrugated brass tubing. However, FAC tubing is made only in lengths of 1 to 6 feet, FAC tubing is made with connectors on each end, and FAC tubing does not have a plastic sheath. On FAC tubing the corrugations are visible.
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Fe – Cr Phase diagram. To qualify as stainless steel, Fe-base alloys must contain at least 10.5% Cr. The iron-chromium phase diagram shows that up to about 13% Cr, the steel undergoes successive transformations upon cooling from the liquid phase from ferritic α phase to austenitic γ phase and back to α.
Tube drawing is a process to size a tube by shrinking a large diameter tube into a smaller one, by drawing the tube through a die. This process produces high-quality tubing with precise dimensions, good surface finish, and the added strength of cold working. [1] For this reason this process is established for many materials, mainly metalworking ...
[6] 953 is based on a specially developed maraging steel stainless steel alloy that can achieve a tensile strength in excess of 2000 MPa (853 is around 1400 MPa), giving a good strength-to-weight ratio. Because of the high strength of the steel, extremely thin tube walls (down to 0.3 mm) can be used, thus reducing the weight. [7]
The average carbon footprint of stainless steel (all grades, all countries) is estimated to be 2.90 kg of CO 2 per kg of stainless steel produced, [88] of which 1.92 kg are emissions from raw materials (Cr, Ni, Mo); 0.54 kg from electricity and steam, and 0.44 kg are direct emissions (i.e., by the stainless steel plant). Note that stainless ...