In the following table, the use row is the value recommended for use in other Wikipedia pages ... 26 Fe iron; use: 1811 K: 1538 °C: 2800 °F WEL: ... melting point ...
J.A. Dean (ed.), Lange's Handbook of Chemistry (15th Edition), McGraw-Hill, 1999; Section 6, Thermodynamic Properties; Table 6.4, Heats of Fusion, Vaporization, and Sublimation and Specific Heat at Various Temperatures of the Elements and Inorganic Compounds
J.A. Dean (ed), Lange's Handbook of Chemistry (15th Edition), McGraw-Hill, 1999; Section 6, Thermodynamic Properties; Table 6.4, Heats of Fusion, Vaporization, and Sublimation and Specific Heat at Various Temperatures of the Elements and Inorganic Compounds
The bulk compounds should be contrasted with nanoparticles which exhibit melting-point depression, meaning that they have significantly lower melting points than the bulk material, and correspondingly lower Tammann and Hüttig temperatures. [4] For instance, 2 nm gold nanoparticles melt at only about 327 °C, in contrast to 1065 °C for a bulk ...
Iron oxide becomes metallic iron at roughly 1250 °C (2282 °F or 1523 K), almost 300 degrees below iron's melting point of 1538 °C (2800 °F or 1811 K). [5] Mercuric oxide becomes vaporous mercury near 550 °C (1022 °F or 823 K), almost 600 degrees above mercury's melting point of -38 °C (-36.4 °F or 235 K), and also above mercury's ...
{{Periodic table (melting point)|state=expanded}} or {{Periodic table (melting point)|state=collapsed}}This template's initial visibility currently defaults to autocollapse, meaning that if there is another collapsible item on the page (a navbox, sidebar, or table with the collapsible attribute), it is hidden apart from its title bar; if not, it is fully visible.
The melting point of the iron oxide is around half that of the metal being cut. As the metal burns, it immediately turns to liquid iron oxide and flows away from the cutting zone. However, some of the iron oxide remains on the workpiece, forming a hard "slag" which can be removed by gentle tapping and/or grinding.
Values are given in terms of temperature necessary to reach the specified pressure. Valid results within the quoted ranges from most equations are included in the table for comparison. A conversion factor is included into the original first coefficients of the equations to provide the pressure in pascals (CR2: 5.006, SMI: -0.875).