Austenite, also known as gamma-phase iron (γ-Fe), is a metallic, non-magnetic allotrope of iron or a solid solution of iron with an alloying element. [1] In plain-carbon steel , austenite exists above the critical eutectoid temperature of 1000 K (727 °C); other alloys of steel have different eutectoid temperatures.
Their sturdy steel frame was constructed on-site and the house was assembled piece-by-piece from a special Lustron Corporation delivery truck. The assembly team, who worked for the local Lustron builder-dealer, followed a special manual from Lustron and were supposed to complete a house in 360 man-hours.
Alloying elements can have an effect on the eutectoid temperature. Manganese and nickel lower the eutectoid temperature and are known as austenite stabilizing elements. With enough of these elements the austenitic structure may form at room temperature. Carbide-forming elements raise the eutectoid temperature and stabilize ferrites. [1]: 395–396
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.
Bainite is a plate-like microstructure that forms in steels at temperatures of 125–550 °C (depending on alloy content). [1] First described by E. S. Davenport and Edgar Bain, [2] [3] it is one of the products that may form when austenite (the face-centered cubic crystal structure of iron) is cooled past a temperature where it is no longer thermodynamically stable with respect to ferrite ...
This is a list of notable Lustron houses. A Lustron house is a home built using enameled metal. There were about 2500 prefabricated homes built in this manner. [1] [2] Numerous Lustron houses have been listed on the National Register of Historic Places. [3]
For a eutectoid steel (0.76% C), between 6 and 10% of austenite, called retained austenite, will remain. The percentage of retained austenite increases from insignificant for less than 0.6% C steel, to 13% retained austenite at 0.95% C and 30–47% retained austenite for a 1.4% carbon steel. A very rapid quench is essential to create martensite.
Steel is used extremely widely in all types of structures, due to its relatively low cost, high strength-to-weight ratio and speed of construction. Steel is a ductile material, which will behave elastically until it reaches yield (point 2 on the stress–strain curve), when it becomes plastic and will fail in a ductile manner (large strains, or ...