Different forms and tempers of 6061 aluminium alloy are discussed in the following standards: [28] ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate; ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes; ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod ...
6063 is the most common alloy used for aluminium extrusion. It allows complex shapes to be formed with very smooth surfaces fit for anodizing and is popular for visible architectural applications such as window frames, door frames, roofs, and sign frames. [3] Applications requiring higher strength typically use 6061 or 6082 instead.
7075 aluminium alloy (AA7075) is an aluminium alloy with zinc as the primary alloying element. It has excellent mechanical properties and exhibits good ductility, high strength, toughness, and good resistance to fatigue.
Note that the term aircraft aluminium or aerospace aluminium usually refers to 7075. [65] [66] 4047 aluminium is a unique alloy used in both the aerospace and automotive applications as a cladding alloy or filler material. As filler, aluminium alloy 4047 strips can be combined to intricate applications to bond two metals. [67]
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.