Tempering is used to precisely balance the mechanical properties of the metal, such as shear strength, yield strength, hardness, ductility, and tensile strength, to achieve any number of a combination of properties, making the steel useful for a wide variety of applications. Tools such as hammers and wrenches require good resistance to abrasion ...
Holloman and Jaffe determined the value of C experimentally by plotting hardness versus tempering time for a series of tempering temperatures of interest and interpolating the data to obtain the time necessary to yield a number of different hardness values. This work was based on six different heats of plain carbon steels with carbon contents ...
The mechanical properties of 7075 depend greatly on the tempering of the material. [7] Aluminum 7075 has a low formability at low room temperature and is vulnerable to stress corrosion cracking. Using different elevated temperature forming techniques has been shown to reduce springback and fracture. [8]
Different forms and tempers of 6061 aluminium alloy are discussed in the following standards: [28] ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate; ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes; ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod ...
The tempering colors can be used to judge the final properties of the tempered steel. Very hard tools are often tempered in the light to the dark straw range, whereas springs are often tempered to the blue. However, the final hardness of the tempered steel will vary, depending on the composition of the steel.
Differential tempering (also called graded tempering, selective tempering or local tempering) is the inverse of differential hardening, to ultimately produce similar results. Differential tempering begins by taking steel that has been uniformly quenched and hardened, and then heating it in localized areas to reduce the hardness.
The term hardened steel is often used for a medium or high carbon steel that has been given heat treatment and then quenching followed by tempering. The quenching results in the formation of metastable martensite , the fraction of which is reduced to the desired amount during tempering.
3003 aluminium alloy is an alloy in the wrought aluminium-manganese family (3000 or 3xxx series). It can be cold worked (but not, unlike some other types of aluminium alloys, heat-treated) to produce tempers with a higher strength but a lower ductility.