Vacuum Assisted Resin Transfer Molding (VARTM) or Vacuum Injected Molding (VIM) is a closed mold, out of autoclave (OOA) [1] composite manufacturing process. VARTM is a variation of Resin Transfer Molding (RTM) with its distinguishing characteristic being the replacement of the top portion of a mold tool with a vacuum bag and the use of a vacuum to assist in resin flow. [2]
The distinctive feature of resin transfer moulding is that the reinforcement materials are placed into this cavity, and before the introduction of the matrix material, the mould set is closed. Resin transfer moulding involves numerous varieties which differ in the mechanics of how the resin is introduced to the reinforcement in the mould cavity.
Transfer molding (BrE: transfer moulding) is a manufacturing process in which casting material is forced into a mold. Transfer molding is different from compression molding in that the mold is enclosed [ 1 ] rather than open to the fill plunger resulting in higher dimensional tolerances and less environmental impact. [ 2 ]
What sets SQRTM apart from standard resin transfer molding is the substitution of a prepreg layup rather than a dry fiber preform. [3] SQRTM is an RTM process adapted to prepreg technology. The prepreg is placed in a closed mold and during the cure cycle, a small amount of resin is injected into the cavity through ports positioned around the part.
Compression molding is a method of molding in which the molding material, generally preheated, is first placed in an open, heated mold cavity. The mold is closed with a top force or plug member, pressure is applied to force the material into contact with all mold areas, while heat and pressure are maintained until the molding material has cured; this process is known as compression molding ...
The difference comes from the application of the fibre and resin material to the mould. Spray-up is an open-moulding composites fabrication process where resin and reinforcements are sprayed onto a reusable mould. The resin and glass may be applied separately or simultaneously "chopped" in a combined stream from a chopper gun.
Glass fiber-reinforced composites comprise the largest segment into which UPRs are used and can be processed via SMC, BMC, pultrusion, cured-in-place pipe (known as relining in Europe), filament winding, vacuum molding, spray-up molding, resin transfer molding (RTM). Wind turbine blades also use them [9] as well as many more processes.
Usually, they are pre-impregnated with the resin in the form of prepreg fabrics or unidirectional tapes. In some situations, a film of resin is placed upon the lower mould, and dry reinforcement is placed above. The upper mould is installed, and the vacuum is applied to the mould cavity. The assembly is placed into an autoclave. This process is ...