6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
Hobby-grade RC models commonly use 7075 and 6061 for chassis plates. 7075 is used in the manufacturing of M16 rifles for the U.S. military as well as AR-15 style rifles for the civilian market. In particular high-quality M16 rifle lower and upper receivers, as well as extension tubes, are typically made from 7075-T6 alloy.
7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]
6013; 6061; 6063; 6113; 6951; 7010; 7049; 7050; 7055; 7068; 7075; 7079; 7093; 7150; 7178; 7475; 8009; Note that the term aircraft aluminium or aerospace aluminium usually refers to 7075. [65] [66] 4047 aluminium is a unique alloy used in both the aerospace and automotive applications as a cladding alloy or filler material.
6105 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the least common of the alloys in this series. While most wrought aluminium alloys are covered by multiple standards (from any mixture of ASTM, EN, ISO, and national standard bodies), 6105 is only dealt with in ASTM B221: Standard Specification for Aluminum and Aluminum-Alloy ...
Alloys with higher copper content (alloyings 6061, 6056, 6013) are mainly used in aviation. Iron occurs in all aluminium alloys as an impurity in quantities of 0.05-0.5%. It forms the phases Al8Fe2Si, Al5FeSi and Al8FeMg3Si6, which are all thermally stable, but undesirable because they brittle the material. Silicon surpluses are also used to ...