Chrome plating (less commonly chromium plating) ... Plating thickness ranges from 5 to 50 μin (0.13 to 1.27 μm). [2] Advantages and disadvantages.
Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [ 1 ] : p.1265 [ 2 ] The coating serves as a corrosion inhibitor , as a primer to improve the adherence of paints and adhesives , [ 2 ] as a decorative finish, or ...
Electroless nickel plating, also known as enickel and NiP, offers many advantages: uniform layer thickness over most complicated surfaces, direct plating of ferrous metals (steel), superior wear and corrosion resistance compared to electroplated nickel or chrome. Much of the chrome plating done in aerospace industry can be replaced with ...
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
Black oxide or blackening is a conversion coating for ferrous materials, stainless steel, copper and copper based alloys, zinc, powdered metals, and silver solder. [1] It is used to add mild corrosion resistance, for appearance, and to minimize light reflection. [ 2 ]
There are two deposition methods: thin, and thick. Thin deposition involves a layer of chromium below 1 μm thickness deposited by chrome plating, and is used for decorative surfaces. Thicker chromium layers are deposited if wear-resistant surfaces are needed.