Hexaferrum and epsilon iron (ε-Fe) are synonyms for the hexagonal close-packed (HCP) phase of iron that is stable only at extremely high pressure. A 1964 study at the University of Rochester mixed 99.8% pure α-iron powder with sodium chloride , and pressed a 0.5-mm diameter pellet between the flat faces of two diamond anvils.
Iron-carbon phase diagram, showing the iron-carbon phase diagram (near the lower left). In iron and steel metallurgy, ledeburite is a mixture of 4.3% carbon in iron and is a eutectic mixture of austenite and cementite. Ledeburite is not a type of steel as the carbon level is too high although it may occur as a separate constituent in some high ...
Steel is between 0 and 2.06 mass percent of carbon. Cast iron is between 2.06 and 6.67%. Black lines indicate the metastable Fe/Fe3Cphase, red is the stable Fe/Carbon phase This diagram is for illustrative purposes only, and is not thermodynamically accurate.
Low-pressure phase diagram of pure iron. BCC is body centered cubic and FCC is face-centered cubic. Iron-carbon eutectic phase diagram, showing various forms of Fe x C y substances. Iron allotropes, showing the differences in structure. The alpha iron (α-Fe) is a body-centered cubic (BCC) and the gamma iron (γ-Fe) is a face-centered cubic (FCC).
Iron-cementite meta-stable diagram. Cast iron's properties are changed by adding various alloying elements, or alloyants. Next to carbon, silicon is the most important alloyant because it forces carbon out of solution. A low percentage of silicon allows carbon to remain in solution, forming iron carbide and producing white cast iron.
Austenite, also known as gamma-phase iron (γ-Fe), is a metallic, non-magnetic allotrope of iron or a solid solution of iron with an alloying element. [1] In plain-carbon steel , austenite exists above the critical eutectoid temperature of 1000 K (727 °C); other alloys of steel have different eutectoid temperatures.
Derivative works of this file: Pure iron phase diagram (EN).png This is a retouched picture , which means that it has been digitally altered from its original version. The original can be viewed here: Diagramma di fase del ferro puro.svg : .
The iron-carbon phase diagram. While cementite is thermodynamically unstable, eventually being converted to austenite (low carbon level) and graphite (high carbon level) at higher temperatures, it does not decompose on heating at temperatures below the eutectoid temperature (723 °C) on the metastable iron-carbon phase diagram.