Brazing has many advantages over other metal-joining techniques, such as welding. Since brazing does not melt the base metal of the joint, it allows much tighter control over tolerances and produces a clean joint without the need for secondary finishing. Additionally, dissimilar metals and non-metals (i.e. metalized ceramics) can be brazed. [2]
Brazing solders are formulated primarily for strength, silver solder is used by jewelers to protect the precious metal and by machinists and refrigeration technicians for its tensile strength but lower melting temperature than brazing, and the primary benefit of soft solder is the low temperature used (to prevent heat damage to electronic ...
Welding a handle onto a pitcher can usually be done with relative ease. However, when welding a tube to another tube, a combination of blowing and suction, and pressing and pulling is used to ensure a good seal, to shape the glass, and to keep the surface tension from closing the tube in on itself. Sometimes a filler rod may be used, but ...
Soldering performed using alloys with a melting point above 450 °C (840 °F; 720 K) is called "hard soldering", "silver soldering", or brazing. In specific proportions, some alloys are eutectic — that is, the alloy's melting point is the lowest possible for a mixture of those components, and coincides with the freezing point.
Brazing and hard soldering use a higher temperature filler that melts at a temperature which may approach that of the base metal, and which may form a eutectic alloy with the base metal. Filler alloys have a lower melting point than the base metal, so that the joint may be made by bringing the whole assembly up to temperature without everything ...
This, as with most forms of electrical welding, simply completes a circuit through which a DC current is passed. The pin tip is the point of highest resistance at which point an arc is drawn, melting the solder flux whilst simultaneously heating the lug material and the surface of the structure or pipeline to the required soldering temperature.