In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
Type 310 310S— is a highly alloyed austenitic stainless steel used for high temperature application. The high chromium and nickel content give the steel excellent oxidation resistance as well as high strength at high temperature. This grade is also very ductile, and has good weldability enabling its widespread usage in many applications. [7]
The ease of welding largely depends on the type of stainless steel used. Austenitic stainless steels are the easiest to weld by electric arc, with weld properties similar to those of the base metal (not cold-worked). Martensitic stainless steels can also be welded by electric-arc but, as the heat-affected zone (HAZ) and the fusion zone (FZ ...
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
A2 stainless steel outside the US, in accordance with ISO 3506 for fasteners. [4] 18/8 and 18/10 stainless steel (also written 18-8 and 18-10) in the commercial tableware and fastener industries. SUS304 the Japanese JIS G4303 equivalent grade. 1.4301, the EN 10088 equivalent. [5] 06Cr19Ni10 and ISC S30408, the equivalent in Chinese GB/T 20878 ...
The two major types of austenitic stainless steels are characterized by the oxide layer that forms on the steel surface: either chromia-forming or alumina-forming. Cr-forming stainless steel is the most common type. However, Cr-forming steels do not exhibit high creep resistance at high temperatures, especially in environments with water vapor.