The addition of an accelerator speeds the setting time and thus cure time starts earlier. [1] This allows concrete to be placed in winter with reduced risk of frost damage. [2] Concrete is damaged if it does not reach a strength of 500 pounds per square inch (3.4 MPa) before freezing. [3]: 19
Accelerated curing is any method by which high early age strength is achieved in concrete. These techniques are especially useful in the prefabrication industry, wherein high early age strength enables the removal of the formwork within 24 hours, thereby reducing the cycle time, resulting in cost-saving benefits. [ 1 ]
Therefore, when concreting at cold temperature cannot be avoided, it is essential to have a minimum curing time at a temperature sufficiently above the freezing point of the concrete pore water, so that the early strength of concrete is high enough to resist the inner tensile stress caused by water freezing. [5]
The surface of vacuum concrete is entirely free from pitting and the uppermost 1/16 inch is highly resistant to abrasion. ... over time into a strong ... curing phase ...
Concrete is a composite material composed of aggregate bonded together with a fluid cement that cures to a solid over time. Concrete is the second-most-used substance in the world after water, [1] and is the most widely used building material. [2] Its usage worldwide, ton for ton, is twice that of steel, wood, plastics, and aluminium combined. [3]
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Engineers usually specify the required compressive strength of concrete, which is normally given as the 28-day compressive strength in megapascals (MPa) or pounds per square inch (psi). Twenty eight days is a long wait to determine if desired strengths are going to be obtained, so three-day and seven-day strengths can be useful to predict the ...
Concrete creep is essentially the sagging of concrete over time. Creep and shrinkage of concrete are two physical properties of concrete.The creep of concrete, which originates from the calcium silicate hydrates (C-S-H) in the hardened Portland cement paste (which is the binder of mineral aggregates), is fundamentally different from the creep of metals and polymers.