ASTM A325 is an ASTM International standard for heavy hex structural bolts, titled Standard Specification for Structural Bolts, Steel, Heat Treated, 120/105 ksi Minimum Tensile Strength. It defines mechanical properties for bolts that range from 1 ⁄ 2 to 1 + 1 ⁄ 2 inches (13 to 38 mm) in diameter. [1]
In engineering, shear strength is the strength of a material or component against the type of yield or structural failure when the material or component fails in shear. A shear load is a force that tends to produce a sliding failure on a material along a plane that is parallel to the direction of the force. When a paper is cut with scissors ...
A bolt with property class 12.9 has a tensile strength of 1200 MPa (1 MPa = 1 N/mm 2) or 1.2 kN/mm 2 and the yield strength is 0.90 times tensile strength, 1080 MPa in this case. A bolt with property class 4.6 has a tensile strength of 400 MPa (1 MPa = 1 N/mm 2) or 0.4 kN/mm 2 and yield strength is 0.60 times tensile strength, 240 MPa in this case.
Strength depends upon material properties. The strength of a material depends on its capacity to withstand axial stress, shear stress, bending, and torsion.The strength of a material is measured in force per unit area (newtons per square millimetre or N/mm², or the equivalent megapascals or MPa in the SI system and often pounds per square inch psi in the United States Customary Units system).
When a shear load is applied, the connected parts move and the bolt shank makes contact with the hole walls, which transfers the load from the parts to the bolt. This causes a shear stress in the bolt at the junction of the connected parts, which it resists through its shear strength. As bearing type joints rely on this direct contact, they are ...
The formula to calculate average shear stress τ or force per unit area is: [1] =, where F is the force applied and A is the cross-sectional area.. The area involved corresponds to the material face parallel to the applied force vector, i.e., with surface normal vector perpendicular to the force.
The strength of materials is determined using various methods of calculating the stresses and strains in structural members, such as beams, columns, and shafts. The methods employed to predict the response of a structure under loading and its susceptibility to various failure modes takes into account the properties of the materials such as its yield strength, ultimate strength, Young's modulus ...
The CRSS is the value of resolved shear stress at which yielding of the grain occurs, marking the onset of plastic deformation. CRSS, therefore, is a material property and is not dependent on the applied load or grain orientation. The CRSS is related to the observed yield strength of the material by the maximum value of the Schmid factor: