2024-O temper aluminium has no heat treating. It has an ultimate tensile strength of 140–210 MPa (21–30 ksi), and maximum yield strength of no more than 97 MPa (14,000 psi). The material has elongation (stretch before ultimate failure) of 10–25%, this is the allowable range per applicable AMS specifications.
Different forms and tempers of 6061 aluminium alloy are discussed in the following standards: [28] ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate; ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes; ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod ...
The retrogression and reage (RRA) temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper, it involves overaging past peak hardness (T6 temper) to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels. [10]
The temper designation follows the cast or wrought designation number with a dash, a letter, and potentially a one to three digit number, e.g. 6061-T6. The definitions for the tempers are: [5] [6]-F : As fabricated-H : Strain hardened (cold worked) with or without thermal treatment -H1 : Strain hardened without thermal treatment
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
5052 is an aluminium–magnesium alloy, primarily alloyed with magnesium and chromium. 5052 is not a heat treatable aluminum alloy, but can be hardened through cold working. [ 2 ] Chemical properties