Chrome plating (less commonly chromium plating) is a technique of electroplating a thin layer of chromium onto a metal object. A chrome plated part is called chrome , or is said to have been chromed .
The chromate coating process starts with a redox reaction between the hexavalent chromium and the metal. [2] In the case of aluminum, for example, Cr 6+ + Al 0 → Cr 3+ + Al 3+ The resulting trivalent cations react with hydroxide ions in water to form the corresponding hydroxides, or a solid solution of both hydroxides: Cr 3+ + 3 OH − → Cr ...
The primary chromium ore is the mixed metal oxide chromite, FeCr 2 O 4, found as brittle metallic black crystals or granules. Chromite ore is heated with a mixture of calcium carbonate and sodium carbonate in the presence of air. The chromium is oxidized to the hexavalent form, while the iron forms iron(III) oxide, Fe 2 O 3:
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
Stainless steel and chrome plating (electroplating with chromium) together comprise 85% of the commercial use. Chromium is also greatly valued as a metal that is able to be highly polished while resisting tarnishing. Polished chromium reflects almost 70% of the visible spectrum, and almost 90% of infrared light. [11]
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...