Basic oxygen steelmaking is a primary steelmaking process for converting molten pig iron into steel by blowing oxygen through a lance over the molten pig iron inside the converter. Exothermic heat is generated by the oxidation reactions during blowing. The basic oxygen steel-making process is as follows:
To reduce the carbon content in pig iron and obtain the desired carbon content of steel, it is re-melted and oxygen is blown through in basic oxygen steelmaking. In this step, the oxygen binds with the undesired carbon, carrying it away in the form of CO 2 gas, an additional emission source. After this step, the carbon content in the pig iron ...
Open-hearth steelmaking had superseded the Bessemer process in UK by 1900, but elsewhere in Europe, especially in Germany, the Bessemer and Thomas processes were used until the late 1960s when they were superseded by basic oxygen steelmaking. The last open-hearth furnace in former East Germany was stopped in 1993. In the US, steel production ...
According to this broad definition, bloomeries for iron, blowing houses for tin, and smelt mills for lead would be classified as blast furnaces. However, the term has usually been limited to those used for smelting iron ore to produce pig iron , an intermediate material used in the production of commercial iron and steel , and the shaft ...
In the 20th century, the US industry successively adopted the open hearth furnace, then the basic oxygen steelmaking process. Since the American industry peaked in the 1940s and 1950s, the US industry has shifted to small mini-mills and specialty mills, using iron and steel scrap as feedstock, rather than iron ore.
The ratios can be done in any number of phases to facilitate the reaction. The gases are usually blown through a top lance (oxygen only) and tuyeres in the sides/bottom (oxygen with an inert gas shroud). The stages of blowing remove carbon by the combination of oxygen and carbon forming CO gas. 4 Cr (bath) + 3 O 2 → 2 Cr 2 O 3
This occurs all throughout as an unintended part of the steelmaking process. Oxygen blowing is a method of steelmaking where oxygen is blown through pig iron to lower the carbon content. Oxygen forms oxides with the unwanted elements, such as carbon, silicon, phosphorus, and manganese, which appear from various stages of the manufacturing ...
Finally, the basic oxygen process was introduced at the Voest-Alpine works in 1952; a modification of the basic Bessemer process, it lances oxygen from above the steel (instead of bubbling air from below), reducing the amount of nitrogen uptake into the steel. The basic oxygen process is used in all modern steelworks; the last Bessemer ...