Accelerated curing is any method by which high early age strength is achieved in concrete.These techniques are especially useful in the prefabrication industry, wherein high early age strength enables the removal of the formwork within 24 hours, thereby reducing the cycle time, resulting in cost-saving benefits. [1]
The addition of an accelerator speeds the setting time and thus cure time starts earlier. [1] This allows concrete to be placed in winter with reduced risk of frost damage. [2] Concrete is damaged if it does not reach a strength of 500 pounds per square inch (3.4 MPa) before freezing. [3]: 19
The early strength of the concrete can be increased if it is kept damp during the curing process. Minimizing stress prior to curing minimizes cracking. High-early-strength concrete is designed to hydrate faster, often by increased use of cement that increases shrinkage and cracking. The strength of concrete changes (increases) for up to three ...
The ultimate strength of concrete is influenced by the water-cementitious ratio (w/cm), the design constituents, and the mixing, placement and curing methods employed.All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. [2]
High-strength concrete has a compressive strength greater than 40 MPa (6000 psi). In the UK, BS EN 206-1 [3] defines High strength concrete as concrete with a compressive strength class higher than C50/60. High-strength concrete is made by lowering the water-cement (W/C) ratio to 0.35 or lower.
The curing of concrete when it continues to harden after its initial setting and progressively develops its mechanical strength is a critical phase to avoid unwanted cracks in concrete. Depending on the temperature (summer or winter conditions) and thus on the cement hydration kinetics controlling the setting and hardening rate of concrete ...
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
The main factors influencing temperature variation in the mass concrete structure are: the size of the structure, the ambient temperature, the initial temperature of the concrete at the time of placement and curing program, the cement type, and the cement contents in the mix.