Electromigration (red arrow) is due to the momentum transfer from the electrons moving in a wire. Electromigration is the transport of material caused by the gradual movement of the ions in a conductor due to the momentum transfer between conducting electrons and diffusing metal atoms.
Stress migration is a failure mechanism that often occurs in integrated circuit metallization (aluminum, copper). Voids form as result of vacancy migration driven by the hydrostatic stress gradient. Large voids may lead to open circuit or unacceptable resistance increase that impedes the IC performance.
Diffusion and electromigration tend to be accelerated by high temperatures, shortening the lifetime of the device; damage to junctions not leading to immediate failure may manifest as altered current–voltage characteristics of the junctions. Electrical overstress failures can be classified as thermally-induced, electromigration-related and ...
Black's Equation is a mathematical model for the mean time to failure (MTTF) of a semiconductor circuit due to electromigration: a phenomenon of molecular rearrangement (movement) in the solid phase caused by an electromagnetic field. The equation is: [1] = ()
Electromigration – electrically induced movement of the materials in the chip; Burnout – localized overstress; Hot Electron Trapping – due to overdrive in power RF circuits; Electrical Stress – Electrostatic discharge, High Electro-Magnetic Fields , Latch-up overvoltage, overcurrent
Dendrite growth requires moisture capable of dissolving the metal into a solution of metal ions, which are then redistributed by electromigration in the presence of an electromagnetic field. While the precise mechanism for whisker formation remains unknown, it is known that whisker formation does not require either dissolution of the metal or ...
Electrochemical migration (ECM) is the dissolution and movement of metal ions in presence of electric potential, which results in the growth of dendritic structures between anode and cathode. The process is most commonly observed in printed circuit boards where it may significantly decrease the insulation between conductors.
Feedback-controlled electromigration (FCE) is an experimental technique to investigate the phenomenon known as electromigration. By controlling the voltage applied as the conductance varies it is possible to keep the voltage at a critical level for electromigration .