In materials science, a general rule of mixtures is a weighted mean used to predict various properties of a composite material. [ 1 ] [ 2 ] [ 3 ] It provides a theoretical upper- and lower-bound on properties such as the elastic modulus , ultimate tensile strength , thermal conductivity , and electrical conductivity . [ 3 ]
Richmann's law, [1] [2] sometimes referred to as Richmann's rule, [3] Richmann's mixing rule, [4] Richmann's rule of mixture [5] or Richmann's law of mixture, [6] is a physical law for calculating the mixing temperature when pooling multiple bodies. [5]
For a fluid mixture, this means that the shear viscosity will also vary according to the fluid composition. To map the viscosity as a function of all these variables require a large sequence of experiments that generates an even larger set of numbers called measured data, observed data or observations. Prior to, or at the same time as, the ...
In crystallography, materials science and metallurgy, Vegard's law is an empirical finding (heuristic approach) resembling the rule of mixtures.In 1921, Lars Vegard discovered that the lattice parameter of a solid solution of two constituents is approximately a weighted mean of the two constituents' lattice parameters at the same temperature: [1] [2]
Reuss (1929) [5] - Stresses constant in composite, rule of mixtures for compliance components. Strength of Materials (SOM) - Longitudinally: strains constant in composite , stresses volume-additive. Transversely: stresses constant in composite, strains volume-additive.
An ideal solution or ideal mixture is a solution that exhibits thermodynamic properties analogous to those of a mixture of ideal gases. [1] The enthalpy of mixing is zero [2] as is the volume change on mixing by definition; the closer to zero the enthalpy of mixing is, the more "ideal" the behavior of the solution becomes.
In chemistry, the lever rule is a formula used to determine the mole fraction (x i) or the mass fraction (w i) of each phase of a binary equilibrium phase diagram. It can be used to determine the fraction of liquid and solid phases for a given binary composition and temperature that is between the liquidus and solidus line.
The equation of state of Soave is defined as follows: = (+). The original α-function has been replaced by the function of Mathias–Copeman: [2] = [+ + + ()].The parameters of the Mathias–Copeman equation are fitted to experimental vapor-pressure data of pure components and provide a better description of the vapor pressure than the original relation.