In the aluminum industry, the process is also called chemical film [13] or yellow iridite, [13] Commercial trademarked names include Iridite [13] and Bonderite [14] (formerly known as Alodine, or Alocrom in the UK). [15] The main standards for chromate conversion coating of aluminium are MIL-DTL-5541 in the US, and Def Stan 03/18 in the UK.
In conventional anodizing, this layer of oxide is grown on the surface of the metal by the application of electrical potential, while the part is immersed in an acidic electrolyte. In plasma electrolytic oxidation, higher potentials are applied. For example, in the plasma electrolytic oxidation of aluminum, at least 200 V must be applied.
The anodizing current varies with the area of aluminium being anodized and typically ranges from 30 to 300 A/m 2. Aluminium anodizing (eloxal or Electrolytic Oxidation of Aluminium) [12] is usually performed in an acidic solution, typically sulphuric acid or chromic acid, which slowly dissolves the aluminium oxide.
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound.
The term "electroplating" is also used occasionally for processes that occur under electro-oxidation (i.e positive or anodic current on the working electrode), although such processes are more commonly referred to as anodizing rather than electroplating.
Black for aluminum. Boil a solution of 20 g ammonium molybdate and 5 g of sodium thiosulfate in a liter of water, immerse the objects, rinse, dry, wax or lacquer after the development of color. [31] Lustre colours. Use a solution of 280 g of sodium thiosulphate, 25 g of cupric acetate and 30 g of citric acid. It can be used on copper and its ...