miscible polymer blends (homogeneous polymer blends): Polymer blend that is a single-phase structure. In this case, one glass transition temperature will be observed. The use of the term polymer alloy for a polymer blend is discouraged, as the former term includes multiphase copolymers but excludes incompatible polymer blends. [3]
In polymer chemistry, compatibilization is the addition of a substance to an immiscible blend of polymers that will increase their stability. Polymer blends are typically described by coarse, unstable phase morphologies; this results in poor mechanical properties. Compatibilizing the system will make a more stable and better blended phase ...
Novel polymeric alloy (NPA) is a polymeric alloy composed of polyolefin and thermoplastic engineering polymer with enhanced engineering properties. NPA was developed for use in geosynthetics . One of the first commercial NPA applications was in the manufacturer of polymeric strips used to form Neoloy® cellular confinement systems (geocells) .
The PPE blends are characterized by hot water resistance with low water absorption, high impact strength, halogen-free fire protection and low density. This plastic is processed by injection molding or extrusion; depending on the type, the processing temperature is 260–300 °C. The surface can be printed, hot-stamped, painted or metallized.
, where ΔS is the change in entropy of mixing, R is the gas constant, Φ is the volume fraction of each polymer, and x is the number of segments of each polymer. [3] x 1 and x 2 increase with higher degrees of polymerization and thus molecular weight. Since most useful polymers are high in molecular weight, the change in entropy experienced ...
Additionally, it can be shown that for a binary blend of polymer species with equal chain lengths (=) the critical concentration should be = /; however, polymers blends have been observed where this parameter is highly asymmetric. In certain blends, mixing entropy can dominate over monomer interaction.
where is the volume fraction of the fibers in the composite (and is the volume fraction of the matrix).. If it is assumed that the composite material behaves as a linear-elastic material, i.e., abiding Hooke's law = for some elastic modulus of the composite and some strain of the composite , then equations 1 and 2 can be combined to give
Suspension polymerization is divided into two main types, depending on the morphology of the particles that result. In bead polymerization, the polymer is soluble in its monomer and the result is a smooth, translucent bead. In powder polymerization, the polymer is not soluble in its monomer and the resultant bead will be porous and irregular. [5]