Case-hardening or carburization is the process of introducing carbon to the surface of a low-carbon iron, or more commonly a low-carbon steel object, in order to harden the surface. Iron which has a carbon content greater than ~0.02% is known as steel .
Quench polish quench (QPQ) is a specialized type of nitrocarburizing case hardening that increases corrosion resistance. It is sometimes known by the brand name of Tufftride, Tenifer or Melonite. [1] Three steps are involved: nitrocarburize ("quench"), polish, and post-oxidize ("quench"). [2]
Nitriding is a heat treating process that diffuses nitrogen into the surface of a metal to create a case-hardened surface. These processes are most commonly used on low-alloy steels. They are also used on titanium, aluminium and molybdenum.
This also inversely affects the depth of the case; i.e., a high carbon steel will form a hard, but shallow case. [14] A similar process is the trademarked "Nu-Tride" process, also known incorrectly as the "Kolene" process (which is the company's name), includes a preheat and an intermediate quench cycle.
A few typical hardening agents include carbon monoxide gas (CO), sodium cyanide and barium carbonate, or hardwood charcoal. In gas carburizing, carbon is given off by propane or natural gas . In liquid carburizing, the carbon is derived from a molten salt composed mainly of sodium cyanide (NaCN) and barium chloride (BaCl 2 ).
The parts are then oil quenched, and the resulting part has a harder case than possibly achieved for carburization, and the addition of the carbonitrided layer increases the residual compressive stresses in the case such that the contact fatigue resistance and strength gradient are both increased. Studies are showing that carbonitriding ...
Surface carburizing, or case hardening, is one example of solid solution strengthening in which the density of solute carbon atoms is increased close to the surface of the steel, resulting in a gradient of carbon atoms throughout the material. This provides superior mechanical properties to the surface of the steel without having to use a ...
Color case hardening is the predecessor of all metal coloring typically employed in the firearms industry. Contemporary heat-treatable steels did not exist or were in their infancy. Soft, low-carbon steel was used, but strong materials were needed for the receivers of firearms. Initially case hardening was used but did not offer any aesthetics.