The Gmelin rare earths handbook lists 1522 °C and 1550 °C as two melting points given in the literature, the most recent reference [Handbook on the chemistry and physics of rare earths, vol.12 (1989)] is given with 1529 °C.
{{Periodic table (melting point)|state=expanded}} or {{Periodic table (melting point)|state=collapsed}}This template's initial visibility currently defaults to autocollapse, meaning that if there is another collapsible item on the page (a navbox, sidebar, or table with the collapsible attribute), it is hidden apart from its title bar; if not, it is fully visible.
The melting point (or, rarely, liquefaction point) of a substance is the temperature at which it changes state from solid to liquid. At the melting point the solid and liquid phase exist in equilibrium. The melting point of a substance depends on pressure and is usually specified at a standard pressure such as 1 atmosphere or 100 kPa.
Of all metals in pure form, tungsten has the highest melting point (3,422 °C, 6,192 °F), lowest vapor pressure (at temperatures above 1,650 °C, 3,000 °F), and the highest tensile strength. [26] Although carbon remains solid at higher temperatures than tungsten, carbon sublimes at atmospheric pressure instead of melting, so it has no melting ...
For the equivalent in degrees Fahrenheit °F, see: Boiling points of the elements (data page) Some values are predictions Primordial From decay Synthetic Border shows natural occurrence of the element
Pewter (/ ˈ p juː t ər /) is a malleable metal alloy consisting of tin (85–99%), antimony (approximately 5–10%), copper (2%), bismuth, and sometimes silver. [1] In the past, it was an alloy of tin and lead , but most modern pewter, in order to prevent lead poisoning , is not made with lead.
Forging temperature is the temperature at which a metal becomes substantially more soft, but is lower than the melting temperature, such that it can be reshaped by forging. [1] Bringing a metal to its forging temperature allows the metal's shape to be changed by applying a relatively small force, without creating cracks.
For a metal, zinc has relatively low melting (419.5 °C) and boiling point (907 °C). [29] The melting point is the lowest of all the d-block metals aside from mercury and cadmium; for this reason among others, zinc, cadmium, and mercury are often not considered to be transition metals like the rest of the d-block metals. [29]