Self-leveling concrete was invented in 1952 by Axel Karlsson from Sweden. The first product was a combination of wood glue, fine sand and cement with additives. [1] It was called flytspackel, which directly translates to "floating putty". The term self-leveling can be traced back to a patent applied by the company Lafarge in 1997. [2]
Self-consolidating concrete or self-compacting concrete (SCC) [1] is a concrete mix which has a low yield stress, high deformability, good segregation resistance (prevents separation of particles in the mix), and moderate viscosity (necessary to ensure uniform suspension of solid particles during transportation, placement (without external compaction), and thereafter until the concrete sets).
Self-drying concrete technology is found in certain cementitious patching and leveling materials and tile-setting mortars used in the flooring industry. Self-drying technology allows the cement mix to consume all of its mix water while curing, eliminating the need for excess water to evaporate prior to installing flooring.
Concrete has a limited lifespan between batching / mixing and curing. This means that ready-mixed concrete should be placed within 30 to 45 minutes of the batching process to hold slump and mix design specifications in the US, [15] though in the UK, environmental and material factors, plus in-transit mixing, allow for up two hours to elapse. [16]
In civil engineering, concrete leveling is a procedure that attempts to correct an uneven concrete surface by altering the foundation that the surface sits upon. It is a cheaper alternative to having replacement concrete poured and is commonly performed at small businesses and private homes as well as at factories, warehouses, airports and on roads, highways and other infrastructure.
During the 1980s, Okamura and his Ph.D. student Kazamasa Ozawa at the University of Tokyo developed self-compacting concrete (SCC) which was cohesive, but flowable and took the shape of the formwork without use of any mechanical compaction. SCC is known as self-consolidating concrete in the United States. SCC is characterized by the following: