Chromate conversion coating or alodine coating is a type of conversion coating used to passivate steel, aluminium, zinc, cadmium, copper, silver, titanium, magnesium, and tin alloys. [1]: p.1265 [2] The coating serves as a corrosion inhibitor, as a primer to improve the adherence of paints and adhesives, [2] as a decorative finish, or to ...
Because electrolytically zinc-plated surfaces provide comparatively little corrosion protection, and in the case of galvanic zinc coatings on high-strength steel (e.g. category 10.9 and 12.9 high-strength bolts) there is a risk of hydrogen embrittlement, the industry needed a better corrosion protection system.
Zinc chromate's main use is in industrial painting as a coating over iron or aluminium materials. [8] It was used extensively on aircraft by the US military, especially during the 1930s and 1940s. It is also used in a variety of paint coatings for the aerospace and automotive industries. [9]
Immersion zinc plating is an electroless (non-electrolytic) coating process that deposits a thin layer of zinc on a less electronegative metal, by immersion in a solution containing a zinc or zincate ions, Zn(OH) 2− 4. A typical use is plating aluminum with zinc prior to electrolytic or electroless nickel plating.
The Cronak process is a conventional chromate conversion coating process developed in 1933 by The New Jersey Zinc Company. [1] It involves immersing a zinc or zinc-plated article for 5 to 15 seconds in a chromate solution, typically prepared from sodium dichromate and sulfuric acid. [2]
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion , to improve the adherence of other coatings, for lubrication , or for aesthetic ...
Galvanization (also spelled galvanisation) [1] is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc. [citation needed]
The process steps can typically involve chromate conversion coating the entire component, followed by a masking of the surface in areas where the chromate coating must remain intact. Beyond that, the chromate coating is then dissolved in unmasked areas. The component can then be anodized, with anodizing taking to the unmasked areas.