If a low-carbon steel is only stressed to some point between the upper and lower yield point then the surface develops Lüder bands. [7] Low-carbon steels contain less carbon than other steels and are easier to cold-form, making them easier to handle. [3] Typical applications of low carbon steel are car parts, pipes, construction, and food cans ...
For a eutectoid steel (0.76% C), between 6 and 10% of austenite, called retained austenite, will remain. The percentage of retained austenite increases from insignificant for less than 0.6% C steel, to 13% retained austenite at 0.95% C and 30–47% retained austenite for a 1.4% carbon steel. A very rapid quench is essential to create martensite.
Austempering is heat treatment that is applied to ferrous metals, most notably steel and ductile iron. In steel it produces a bainite microstructure whereas in cast irons it produces a structure of acicular ferrite and high carbon, stabilized austenite known as ausferrite. It is primarily used to improve mechanical properties or reduce ...
Tempering is often used on carbon steels, producing much the same results. The process, called "normalize and temper", is used frequently on steels such as 1045 carbon steel, or most other steels containing 0.35 to 0.55% carbon. These steels are usually tempered after normalizing, to increase the toughness and relieve internal stresses.
Iron-carbon phase diagram, showing the conditions under which austenite (γ) is stable in carbon steel. Allotropes of iron; alpha iron and gamma iron. Austenite, also known as gamma-phase iron (γ-Fe), is a metallic, non-magnetic allotrope of iron or a solid solution of iron with an alloying element. [1]
Virtually generated microstructure of dual-phase steel. [1]Dual-phase steel (DP steel) is a high-strength steel that has a ferritic–martensitic microstructure. DP steels are produced from low or medium carbon steels that are quenched from a temperature above A 1 but below A 3 determined from continuous cooling transformation diagram.