Line defects can be described by gauge theories. Dislocations are linear defects, around which the atoms of the crystal lattice are misaligned. [14] There are two basic types of dislocations, the edge dislocation and the screw dislocation. "Mixed" dislocations, combining aspects of both types, are also common. An edge dislocation is shown. The ...
In materials science, a dislocation or Taylor's dislocation is a linear crystallographic defect or irregularity within a crystal structure that contains an abrupt change in the arrangement of atoms. The movement of dislocations allow atoms to slide over each other at low stress levels and is known as glide or slip .
Glissile dislocations contribute to slip and hardening, but sessile dislocations contribute only to latent hardening. [5] Diffraction methods cannot generally resolve the slip plane of a residual dislocation. For example, in Zr, the screw components of 𝑎 dislocations could slip on prismatic, basal, or 1st-order pyramidal planes.
PSB structure (adopted from [7]). Persistent slip-bands (PSBs) are associated with strain localisation due to fatigue in metals and cracking on the same plane. Transmission electron microscopy (TEM) and three-dimensional discrete dislocation dynamics (DDD [8]) simulation were used to reveal and understand dislocations type and arrangement/patterns to relate it to the sub-surface structure.
The principal direction in which dislocation takes place are defined by a combination of slip planes and weak crystallographic orientations resulting from vacancies and imperfections in the atomic structure. [2] Each dislocation causes a part of the crystal to shift by one lattice point along the slip plane, relative to the rest of the crystal.
Formation of two disclinations (right) out of a dislocation (left) on an otherwise hexagonal background. In 2D, disclinations and dislocations are point defects instead of line defects as in 3D. They are topological defects and play a central role in melting of 2D crystals within the KTHNY theory, based on two Kosterlitz–Thouless transitions.
In metallurgy, recovery is a process by which a metal or alloy's deformed grains can reduce their stored energy by the removal or rearrangement of defects in their crystal structure. These defects, primarily dislocations , are introduced by plastic deformation of the material and act to increase the yield strength of a material.
They can be formed during crystal growth, during plastic deformation as partial dislocations move as a result of dissociation of a perfect dislocation, or by condensation of point defects during high-rate plastic deformation. [3] The start and finish of a stacking fault are marked by partial line dislocations such as a partial edge dislocation.