Electrogalvanizing is a process in which a layer of zinc is bonded to steel to protect against corrosion, enhance adhesion, or give an aesthetic appeal.The process involves electroplating, running a current of electricity through a saline-/zinc-based electrolytic solution with a zinc anode and steel cathode.
Galvanized surface with visible spangle. Galvanization (also spelled galvanisation) [1] is the process of applying a protective zinc coating to steel or iron, to prevent rusting. The most common method is hot-dip galvanizing, in which the parts are coated by submerging them in a bath of hot, molten zinc. [citation needed]
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound. These coatings are commonly applied to protect the part against corrosion , to improve the adherence of other coatings, for lubrication , or for aesthetic ...
The process of hot-dip galvanizing results in a metallurgical bond between zinc and steel, with a series of distinct iron-zinc alloys. The resulting coated steel can be used in much the same way as uncoated. A typical hot-dip galvanizing line operates as follows: [2] Steel is cleaned using a caustic solution. This removes oil/grease, dirt, and ...
Because electrolytically zinc-plated surfaces provide comparatively little corrosion protection, and in the case of galvanic zinc coatings on high-strength steel (e.g. category 10.9 and 12.9 high-strength bolts) there is a risk of hydrogen embrittlement, the industry needed a better corrosion protection system.
Production of galvannealed sheet steel begins with hot dip galvanization of sheet steel. After passing through the galvanizing zinc bath the sheet steel passes through air knives to remove excess zinc, and is then heated in an annealing furnace for several seconds causing iron and zinc layers to diffuse into one another causing the formation of zinc-iron alloy layers at the surface.
Mechanical plating, also known as peen plating, mechanical deposition, or impact plating, is a plating process that imparts the coating by cold welding fine metal particles to a workpiece. Mechanical galvanization is the same process, but applies to coatings that are thicker than 0.001 in (0.025 mm). [ 1 ]
In the case of titanium, niobium, and stainless steel, the colour formed is dependent on the thickness of the oxide (which is determined by the anodizing voltage). Chemically coloring a metal is distinct from simply coating it using a method such as gilding or mercury silvering , because chemical coloring involves a chemical reaction, whereas ...