Only calcium silicates contribute to the strength. Tricalcium silicate is responsible for most of the early strength (first 7 days). [3] Dicalcium silicate, which reacts more slowly, only contributes to late strength. Calcium silicate hydrate (also shown as C-S-H) is a result of the reaction between the silicate phases of Portland cement and water.
Tobermorite is often used in thermodynamical calculations to represent the pole of the most evolved calcium silicate hydrate (C-S-H). According to its chemical formula, its atomic Ca/Si or molar CaO/SiO 2 (C/S) ratio is 5/6 (0.83). Jennite represents the less evolved pole with a C/S ratio of 1.50 (9/6).
Calcium-silicate passive fire protection board being clad around steel structure in order to achieve a fire-resistance rating. Calcium silicate is commonly used as a safe alternative to asbestos for high-temperature insulation materials. Industrial-grade piping and equipment insulation is often fabricated from calcium silicate.
The hydrate is referred to as the calcium silicate hydrate – "C-S-H-" – phase. It grows as a mass of interlocking needles that provide the strength of the hydrated cement system. High alite reactivity is desirable in Portland cement manufacture, and this is achieved by retaining, as far as possible, high temperature polymorphs, in crystals ...
Cement hydration and strength development mainly depend on two silicate phases: tricalcium silicate (C 3 S) , and dicalcium silicate (C 2 S) . [1] Upon hydration, the main reaction products are calcium silicate hydrates (C-S-H) and calcium hydroxide Ca(OH) 2, written as CH in the cement chemist notation. C-S-H is the phase playing the role of ...
Calcium silicate hydrate: C-A-H: Phase more complex than C-S-H: Calcium aluminate hydrate C-A-S-H: This is even more complex than C-S-H and C-A-H: Calcium aluminate silicate hydrate AFt: C 6 A S 3 H 32, sometimes with substitution of Fe for Al, and/or CO 2− 3 for SO 2− 4: Calcium trisulfoaluminate hydrate, or ettringite: AFm
Jennite is often used in thermodynamical calculations to represent the pole of the less evolved calcium silicate hydrate (C-S-H). The value of its atomic Ca/Si or molecular CaO/SiO 2 (C/S) ratio is 1.50 (9/6), as directly calculated from its elementary composition formula. Tobermorite represents the more evolved pole with a C/S ratio of 0.83 (5/6).