Steelmaking is the process of producing steel from iron ore and/or scrap. Steel has been made for millennia, and was commercialized on a massive scale in the 1850s and 1860s, using the Bessemer and Siemens-Martin processes. Two major commercial processes are used.
U.S. Steel and Bethlehem Steel introduced the oxygen process in 1964. [3] By 1970, half of the world's and 80% of Japan's steel output was produced in oxygen converters. [3] In the last quarter of the 20th century, use of basic oxygen converters for steel production was gradually, partially replaced by the electric arc furnace using scrap steel ...
Direct reduction processes can be divided roughly into two categories: gas-based and coal-based. In both cases, the objective of the process is to remove the oxygen contained in various forms of iron ore (sized ore, concentrates, pellets, mill scale, furnace dust, etc.) in order to convert the ore to metallic iron, without melting it (below 1,200 °C (2,190 °F)).
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots. Since then, "continuous casting" has ...
The replacement of charcoal with coal in the steel-making process revolutionized the industry, and tied steelmaking to coal-mining areas. In the 1800s, making a ton of steel required a greater weight of coal than iron ore. Therefore, it was more economical to locate closer to the coal mines.
The process also decreased the labor requirements for steel-making. Before it was introduced, steel was far too expensive to make bridges or the framework for buildings and thus wrought iron had been used throughout the Industrial Revolution. After the introduction of the Bessemer process, steel and wrought iron became similarly priced, and ...
Steel is an alloy composed of between 0.2 and 2.0 percent carbon, with the balance being iron. From prehistory through the creation of the blast furnace, iron was produced from iron ore as wrought iron, 99.82–100 percent Fe, and the process of making steel involved adding carbon to iron, usually in a serendipitous manner, in the forge, or via the cementation process.
Argonoxygen decarburization (AOD) is a process primarily used in stainless steel making and other high grade alloys with oxidizable elements such as chromium and aluminium. After initial melting the metal is then transferred to an AOD vessel where it will be subjected to three steps of refining; decarburization , reduction , and desulfurization .