In making crucible steel, the blister steel bars were broken into pieces and melted in small crucibles, each containing 20 kg or so. This produced higher quality metal, but increased the cost. The Bessemer process reduced the time needed to make lower-grade steel to about half an hour while requiring only enough coke needed to melt the pig iron.
The basic oxygen steel-making process is as follows: Molten pig iron (sometimes referred to as "hot metal") from a blast furnace is poured into a large refractory-lined container called a ladle . The metal in the ladle is sent directly for basic oxygen steelmaking or to a pretreatment stage where sulfur , silicon , and phosphorus are removed ...
The process also decreased the labor requirements for steel-making. Before it was introduced, steel was far too expensive to make bridges or the framework for buildings and thus wrought iron had been used throughout the Industrial Revolution. After the introduction of the Bessemer process, steel and wrought iron became similarly priced, and ...
The primary advantage of the early blast furnace was in large scale production and making iron implements more readily available to peasants. [26] Cast iron is more brittle than wrought iron or steel, which required additional fining and then cementation or co-fusion to produce, but for menial activities such as farming it sufficed.
Continuous casting, also called strand casting, is the process whereby molten metal is solidified into a "semifinished" billet, bloom, or slab for subsequent rolling in the finishing mills. Prior to the introduction of continuous casting in the 1950s, steel was poured into stationary molds to form ingots. Since then, "continuous casting" has ...
The process begins by preparing the puddling furnace. This involves bringing the furnace to a low temperature and then fettling it. Fettling is the process of painting the grate and walls around it with iron oxides, typically hematite; [11] this acts as a protective coating keeping the melted metal from burning through the furnace. Sometimes ...
In these processes, pig iron made from raw iron ore was refined (fined) in a finery forge to produce bar iron, which was then used in steel-making. [52] The production of steel by the cementation process was described in a treatise published in Prague in 1574 and was in use in Nuremberg from 1601.
Argonoxygen decarburization (AOD) is a process primarily used in stainless steel making and other high grade alloys with oxidizable elements such as chromium and aluminium. After initial melting the metal is then transferred to an AOD vessel where it will be subjected to three steps of refining; decarburization , reduction , and desulfurization .