ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3). ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M.
Material take off is not limited to the amount of required material, but also the weight of the items taken off. This is important when dealing with larger structures, allowing the company that does the take off to determine total weight of the item and how best to move the item (if necessary) when construction is completed.
In Canada, steel I-beams are now commonly specified using the depth and weight of the beam in metric terms. For example, a "W250x33" beam is approximately 250 millimetres (9.8 in) in depth (height of the I-beam from the outer face of one flange to the outer face of the other flange) and weighs approximately 33 kg/m (22 lb/ft; 67 lb/yd). [ 8 ]
The austenizing temperature, the temperature where a steel transforms to an austenite crystal structure, for steel starts at 900 °C (1,650 °F) for pure iron, then, as more carbon is added, the temperature falls to a minimum 724 °C (1,335 °F) for eutectic steel (steel with only .83% by weight of carbon in it).
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [7] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada. Another related standard is ASTM A501, which is a ...
Carbon structural steel A36 36 58-80 1.61 23 A36 50 70 1.4 21 High-strength low-alloy Structural steel A242 46 67 1.46 21 Low and intermediate tensile strength carbon steel plates A283 A 24 45-60 1.88 30 B 27 50-65 1.85 28 C 30 55-75 1.83 25 D 33 60-80 1.82 23 Cold-formed welded and seamless carbon steel structural tubing in rounds and shapes A500
Steel is used extremely widely in all types of structures, due to its relatively low cost, high strength-to-weight ratio and speed of construction. Steel is a ductile material, which will behave elastically until it reaches yield (point 2 on the stress–strain curve), when it becomes plastic and will fail in a ductile manner (large strains, or ...