After Corning Glass Works introduced Pyrex in 1915, the name became synonymous with borosilicate glass in the English-speaking world (since the 1940s, a sizable portion of glass produced under the Pyrex brand has also been made of soda–lime glass). Borosilicate glass is the name of a glass family with various members tailored to completely ...
The manufacturing process for soda–lime glass consists in melting the raw materials, which are the silica, soda (Na 2 O), hydrated lime (Ca(OH) 2), dolomite (CaMg(CO 3) 2, which provides the magnesium oxide), and aluminium oxide; along with small quantities of fining agents (e.g., sodium sulfate (Na 2 SO 4), sodium chloride (NaCl), etc.) in a glass furnace at temperatures locally up to 1675 ...
Soda–lime glass (for containers) [2] Borosilicate (low expansion, similar to Pyrex, Duran) Glass wool (for thermal insulation) Special optical glass (similar to Lead crystal) Fused silica Germania glass Germanium selenide glass Chemical composition, wt% 74 SiO 2, 13 Na 2 O, 10.5 CaO, 1.3 Al 2 O 3, 0.3 K 2 O, 0.2 SO 3, 0.2 MgO, 0.01 TiO 2, 0. ...
Pyrex (trademarked as PYREX and pyrex) is a brand introduced by Corning Inc. in 1915, initially for a line of clear, low-thermal-expansion borosilicate glass used for laboratory glassware and kitchenware. It was later expanded in the 1930s to include kitchenware products made of soda–lime glass and other materials. [1]
A Pyrex borosilicate glass measuring cup. Borosilicate glasses (e.g. Pyrex, Duran) typically contain 5–13% boron trioxide (B 2 O 3). [75] Borosilicate glasses have fairly low coefficients of thermal expansion (7740 Pyrex CTE is 3.25 × 10 −6 /°C [78] as compared to about 9 × 10 −6 /°C for a typical soda–lime glass [79]).
Also unlike toughened glass, chemically strengthened glass may be cut after strengthening, but loses its added strength within approximately 20 mm of the cut. Similarly, when the surface of chemically strengthened glass is deeply scratched, this area loses its additional strength. Another negative of chemically strengthened glass is the added cost.
These materials also impart various other properties to the glass that may be beneficial in different applications. The first type of glass used for fiber was soda lime glass or A-glass ("A" for the alkali it contains). It is not very resistant to alkali. A newer, alkali-free (<2%) type, E-glass, is an alumino-borosilicate glass. [10]
Several glasses are utilized in transparent armor, such as normal plate glass (soda-lime-silica), borosilicate glasses, and fused silica. Plate glass has been the most common glass used due to its low cost, but greater requirements for the optical properties and ballistic performance have generated the need for new materials.