Rosin used as flux for soldering A flux pen used for electronics rework Multicore solder containing flux Wire freshly coated with solder, held above molten rosin flux. In metallurgy, a flux is a chemical reducing agent, flowing agent, or purifying agent. Fluxes may have more than one function at a time.
Irregular wire feed – typically a mechanical problem. Porosity – the gases (specifically those from the flux-core) don’t escape the welded area before the metal hardens, leaving holes in the welded metal. More costly filler material/wire as compared to GMAW. The amount of smoke generated can far exceed that of SMAW, GMAW, or GTAW. [2]
Fusion welding is a generic term for welding processes that rely on melting to join materials of similar compositions and melting points. [1] Due to the high-temperature phase transitions inherent to these processes, a heat-affected zone is created in the material [ 1 ] : 755 (although some techniques, like beam welding , often minimize this ...
Along with the wire electrode, a shielding gas feeds through the welding gun, which shields the process from atmospheric contamination. The process can be semi-automatic or automatic. A constant voltage, direct current power source is most commonly used with GMAW, but constant current systems, as well as alternating current, can be used. There ...
The flux also serves the purpose of cleaning any contamination left on the brazing surfaces. Flux can be applied in any number of forms including flux paste, liquid, powder or pre-made brazing pastes that combine flux with filler metal powder. Flux can also be applied using brazing rods with a coating of flux, or a flux core.
A related process, flux-cored arc welding (FCAW), uses similar equipment but uses wire consisting of a steel electrode surrounding a powder fill material. This cored wire is more expensive than the standard solid wire and can generate fumes and/or slag, but it permits even higher welding speed and greater metal penetration.