Cast iron is not malleable even when hot, but it can be formed by casting as it has a lower melting point than steel and good castability properties. [5] Certain compositions of cast iron, while retaining the economies of melting and casting, can be heat treated after casting to make malleable iron or ductile iron objects.
Mild steel (carbon steel with up to about 0.2 wt% C) consists mostly of α-Fe and increasing amounts of cementite (Fe 3 C, an iron carbide). The mixture adopts a lamellar structure called pearlite . Since bainite and pearlite each contain α-Fe as a component, any iron-carbon alloy will contain some amount of α-Fe if it is allowed to reach ...
In the modern world, iron alloys, such as steel, stainless steel, cast iron and special steels, are by far the most common industrial metals, due to their mechanical properties and low cost. The iron and steel industry is thus very important economically, and iron is the cheapest metal, with a price of a few dollars per kilogram or pound.
Steel is made from iron and carbon. Cast iron is a hard, brittle material that is difficult to work, whereas steel is malleable, relatively easily formed and versatile. On its own, iron is not strong, but a low concentration of carbon – less than 1 percent, depending on the kind of steel – gives steel strength and other important properties.
Wrought iron is an iron alloy with a very low carbon content (less than 0.05%) in contrast to that of cast iron (2.1% to 4.5%). It is a semi-fused mass of iron with fibrous slag inclusions (up to 2% by weight), which give it a wood-like "grain" that is visible when it is etched, rusted, or bent to failure.
As a result, the properties of ductile cast iron are that of a spongy steel without the stress concentration effects that flakes of graphite would produce. The carbon percentage present is 3-4% and percentage of silicon is 1.8-2.8%.Tiny amounts of 0.02 to 0.1% magnesium , and only 0.02 to 0.04% cerium added to these alloys slow the growth of ...
Pig iron, also known as crude iron, is an intermediate good used by the iron industry in the production of steel. It is developed by smelting iron ore in a blast furnace . Pig iron has a high carbon content, typically 3.8–4.7 %, [ 1 ] along with silica and other dross , which makes it brittle and not useful directly as a material except for ...
The properties of steel depend on its microstructure: the arrangement of different phases, some harder, some with greater ductility. At the atomic level, the four phases of auto steel include martensite (the hardest yet most brittle), bainite (less hard), ferrite (more ductile), and austenite (the most ductile). The phases are arranged by ...