[1] [2] Nylon 46 is an aliphatic polyamide formed by the polycondensation of two monomers, one containing 4 carbon atoms, 1,4-diaminobutane , and the other 6 carbon atoms, adipic acid, which give nylon 46 its name. It has a higher melting point than nylon 6 or nylon 66 and mainly used in applications which must withstand high temperatures.
FEP; CAS Registry Number: 25067-11-2 Density [1] 2150 kg/m 3: Flexural modulus(E) 586 M Pa: Tensile strength(t) 23 M Pa: Elongation @ break 325% Folding endurance Varies Notch test Melting point: 260 °C Maximum operating temperature 204 °C Water absorption (ASTM) <0.01 % after 24 hours Dielectric constant (Dk) at 1M Hz: 2.1 Dissipation factor
The 428 °F (220 °C) melting point of nylon 6 is lower than the 509 °F (265 °C) melting point of nylon 66. [61] Homopolymer nylons are derived from one monomer. Monomer
The glass transition temperature of Nylon 6 is 47 °C. As a synthetic fibre, Nylon 6 is generally white but can be dyed in a solution bath prior to production for different color results. Its tenacity is 6–8.5 gf/D with a density of 1.14 g/cm 3. Its melting point is at 215 °C and can protect heat up to 150 °C on average. [4]
Nylon 12 exhibits properties between short chain aliphatic nylons (e.g., nylon 6 and nylon 66) and polyolefins. [3] At 178-180 °C, the melting point of nylon 12 is the lowest among the important polyamides. Its mechanical properties, such as hardness, tensile strength, and resistance to abrasion, are similar to those of nylon 6 and nylon 66.
Tests showed the substance was resistant to corrosion from most acids, bases and solvents and had better high temperature stability than any other plastic. By early 1941, a crash program was making substantial quantities of PTFE for the Manhattan Project. [1] [2] [3] [4]
Nylon 66 (loosely written nylon 6-6, nylon 6/6, nylon 6,6, or nylon 6:6) is a type of polyamide or nylon. It, and nylon 6 , are the two most common for textile and plastic industries. Nylon 66 is made of two monomers each containing 6 carbon atoms, hexamethylenediamine and adipic acid , which give nylon 66 its name. [ 1 ]
Melting point: 1 to 3 °C; 34 to 37 °F; 274 to 276 K ... is an important precursor to the polymer nylon 66. In 2005, about one million tonnes of adiponitrile were ...