Concrete is a brittle material and can only withstand small amount of tensile strain due to stress before cracking. When a reinforced concrete member is put in tension, after cracking, the member elongates by widening of cracks and by formation of new cracks. Figure 1 Formation of internal cracks
The curing of concrete when it continues to harden after its initial setting and progressively develops its mechanical strength is a critical phase to avoid unwanted cracks in concrete. Depending on the temperature (summer or winter conditions) and thus on the cement hydration kinetics controlling the setting and hardening rate of concrete ...
Frost damage can occur as cracks, stone splinters and swelling of the material. When water freezes, the volume of water increases by 9 %. [citation needed] When the volumetric moisture content exceeds 91 %, then the volume increase of water in the pores of the material caused by freezing cannot be absorbed by sufficient empty pores. This causes ...
Concrete has a very low coefficient of thermal expansion, and as it matures concrete shrinks. All concrete structures will crack to some extent, due to shrinkage and tension. Concrete which is subjected to long-duration forces is prone to creep. The density of concrete varies, but is around 2,400 kilograms per cubic metre (150 lb/cu ft). [1]
Cracking of the concrete section is nearly impossible to prevent; however, the size and location of cracks can be limited and controlled by appropriate reinforcement, control joints, curing methodology and concrete mix design. Cracking can allow moisture to penetrate and corrode the reinforcement.
Typical crack pattern of the alkali-silica reaction (ASR). The gel exudations through the concrete cracks have a characteristic yellow color and a high pH. The fatty aspect of the exudations imbibing the concrete porosity along the cracks is also a distinctive feature of ASR. The alkali-silica reaction as a chemical cycle process