Iron-carbon phase diagram, showing the conditions under which austenite (γ) is stable in carbon steel. Allotropes of iron; alpha iron and gamma iron Austenite , also known as gamma-phase iron ( γ-Fe ), is a metallic, non-magnetic allotrope of iron or a solid solution of iron with an alloying element. [ 1 ]
The primary phase of low-carbon or mild steel and most cast irons at room temperature is ferromagnetic α-Fe. [8] [9] It has a hardness of approximately 80 Brinell. [10] [11] The maximum solubility of carbon is about 0.02 wt% at 727 °C (1,341 °F) and 0.001% at 0 °C (32 °F). [12] When it dissolves in iron, carbon atoms occupy interstitial ...
Martensite is formed in carbon steels by the rapid cooling of the austenite form of iron at such a high rate that carbon atoms do not have time to diffuse out of the crystal structure in large enough quantities to form cementite (Fe 3 C). Austenite is gamma-phase iron (γ-Fe), a solid solution of iron and alloying elements.
In carbon steel, cementite precipitates from austenite as austenite transforms to ferrite on slow cooling, or from martensite during tempering. An intimate mixture with ferrite, the other product of austenite, forms a lamellar structure called pearlite. The iron-carbon phase diagram
In steel it produces a bainite microstructure whereas in cast irons it produces a structure of acicular ferrite and high carbon, stabilized austenite known as ausferrite. It is primarily used to improve mechanical properties or reduce / eliminate distortion. Austempering is defined by both the process and the resultant microstructure.
Convergent beam electron diffraction (CBED) transmission electron micrograph of a [111] zone axis of austenitic stainless steel. Austenitic stainless steel is one of the five families of stainless steel (along with ferritic, martensitic, duplex and precipitation hardened). [1] Its primary crystalline structure is austenite (face-centered cubic).
Pearlite is a two-phased, lamellar (or layered) structure composed of alternating layers of ferrite (87.5 wt%) and cementite (12.5 wt%) that occurs in some steels and cast irons. During slow cooling of an iron-carbon alloy, pearlite forms by a eutectoid reaction as austenite cools below 723 °C (1,333 °F) (the eutectoid temperature). Pearlite ...
[8] [9] Gamma phase is austenitic with a face-centred cubic (FCC) structure, Fm ¯ m [259] space group, and 3.66 Å lattice parameter. It normally has more nickel, copper, and interstitial carbon and nitrogen. [10] Plastic deformation occurs in austenite more readily than in ferrite.