Guitar slide made of borosilicate glass. Borosilicate glass is a type of glass with silica and boron trioxide as the main glass-forming constituents. Borosilicate glasses are known for having very low coefficients of thermal expansion (≈3 × 10 −6 K −1 at 20 °C), making them more resistant to thermal shock than any other common glass.
Soda–lime glass (for containers) [2] Borosilicate (low expansion, similar to Pyrex, Duran) Glass wool (for thermal insulation) Special optical glass (similar to Lead crystal) Fused silica Germania glass Germanium selenide glass Chemical composition, wt% 74 SiO 2, 13 Na 2 O, 10.5 CaO, 1.3 Al 2 O 3, 0.3 K 2 O, 0.2 SO 3, 0.2 MgO, 0.01 TiO 2, 0. ...
These thermal greases have low electrical conductivity and their volume resistivities are 1.5⋅10 15, 1.8⋅10 11, and 9.9⋅10 9 Ω⋅cm for 860, 8616 and 8617 respectively. The thermal grease 860 is a silicone oil with a Zinc Oxide filler and 8616 and 8617 are synthetic oils with various fillers including Aluminum Oxide and Boron Nitride.
The coefficient of thermal expansion (CTE) of the processed glass needs to be similar to those of the bonding partner. [2] Anodic bonding can be applied with glass wafers at temperatures of 250 to 400 °C or with sputtered glass at 400 °C. [3] Structured borosilicate glass layers may also be deposited by plasma-assisted e-beam evaporation. [4]
A Pyrex borosilicate glass measuring cup. Borosilicate glasses (e.g. Pyrex, Duran) typically contain 5–13% boron trioxide (B 2 O 3). [75] Borosilicate glasses have fairly low coefficients of thermal expansion (7740 Pyrex CTE is 3.25 × 10 −6 /°C [78] as compared to about 9 × 10 −6 /°C for a typical soda–lime glass [79]).
A number of materials contract on heating within certain temperature ranges; this is usually called negative thermal expansion, rather than "thermal contraction".For example, the coefficient of thermal expansion of water drops to zero as it is cooled to 3.983 °C (39.169 °F) and then becomes negative below this temperature; this means that water has a maximum density at this temperature, and ...
Materials with zero or extremely low coefficient of thermal expansion. ... Pages in category "Low thermal expansion materials" ... Borosilicate glass; G. Glucydur; H.
Thermal shock resistance measures can be used for material selection in applications subject to rapid temperature changes. The maximum temperature jump, , sustainable by a material can be defined for strength-controlled models by: [4] [3] = where is the failure stress (which can be yield or fracture stress), is the coefficient of thermal expansion, is the Young's modulus, and is a constant ...