Fiberglass (American English) or fibreglass (Commonwealth English) is a common type of fiber-reinforced plastic using glass fiber.The fibers may be randomly arranged, flattened into a sheet called a chopped strand mat, or woven into glass cloth.
Glass wool, which is one product called "fiberglass" today, was invented some time between 1932 and 1933 by Games Slayter of Owens-Illinois, as a material to be used as thermal building insulation. [1] It is marketed under the trade name Fiberglas, which has become a genericized trademark. Glass fiber, when used as a thermal insulating material ...
FR-4 is a composite material composed of woven fiberglass cloth with an epoxy resin binder that is flame resistant (self-extinguishing). "FR" stands for "flame retardant", and does not denote that the material complies with the standard UL94V-0 unless testing is performed to UL 94, Vertical Flame testing in Section 8 at a compliant lab. The ...
The density of glass varies with chemical composition with values ranging from 2.2 grams per cubic centimetre (2,200 kg/m 3) for fused silica to 7.2 grams per cubic centimetre (7,200 kg/m 3) for dense flint glass. [69]
— "Values ranging from 21.3 to 21.5 gm/cm 3 at 20 °C have been reported for the density of annealed platinum; the best value being about 21.45 gm/cm 3 at 20 °C." 21.46 g/cm 3 — Rose, T. Kirke. The Precious Metals, Comprising Gold, Silver and Platinum .
G-10 or garolite is a high-pressure fiberglass laminate, a type of composite material. [1] It is created by stacking multiple layers of glass cloth, soaked in epoxy resin, then compressing the resulting material under heat until the epoxy cures. [2] [3] It is manufactured in flat sheets, most often a few millimeters thick.
This is a list of some physical properties of common glasses. Unless otherwise stated, the technical glass compositions and many experimentally determined properties are taken from one large study. [1]
The SI unit for specific strength is Pa⋅m 3 /kg, or N⋅m/kg, which is dimensionally equivalent to m 2 /s 2, though the latter form is rarely used. Specific strength has the same units as specific energy , and is related to the maximum specific energy of rotation that an object can have without flying apart due to centrifugal force .