In chemistry, the lever rule is a formula used to determine the mole fraction (x i) or the mass fraction (w i) of each phase of a binary equilibrium phase diagram.It can be used to determine the fraction of liquid and solid phases for a given binary composition and temperature that is between the liquidus and solidus line.
English: Aluminium silicon binary phase diagram for foundry. α: solid solution of silicon in aluminium (cfc, a = 4.04 Å); β: solid solution of aluminium in silicon (cfc, a = 5.43 Å). In the case of Alpax, the eutectic is shifted to 12.1 at% Si (12.5 wt%) due to the presence of sodium.
Equilibrium exists at the solid-liquid interface, and so compositions from the phase diagram are valid Solidus and liquidus are straight segments The fourth condition (straight solidus/liquidus segments) may be relaxed when numerical techniques are used, such as those used in CALPHAD software packages, though these calculations rely on ...
Another type of binary phase diagram is a boiling-point diagram for a mixture of two components, i. e. chemical compounds. For two particular volatile components at a certain pressure such as atmospheric pressure , a boiling-point diagram shows what vapor (gas) compositions are in equilibrium with given liquid compositions depending on temperature.
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.
A phase diagram for a fictitious binary chemical mixture (with the two components denoted by A and B) used to depict the eutectic composition, temperature, and point. ( L denotes the liquid state.) A eutectic system or eutectic mixture ( / j uː ˈ t ɛ k t ɪ k / yoo- TEK -tik ) [ 1 ] is a type of a homogeneous mixture that has a melting point ...
In thermodynamics, the phase rule is a general principle governing multi-component, multi-phase systems in thermodynamic equilibrium.For a system without chemical reactions, it relates the number of freely varying intensive properties (F) to the number of components (C), the number of phases (P), and number of ways of performing work on the system (N): [1] [2] [3]: 123–125