Tempered or toughened glass is a type of safety glass processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. Tempering puts the outer surfaces into compression and the interior into tension .
Toughened glass was invented in 1874 by Francois Barthelemy Alfred Royer de la Bastie. [1] Wire mesh glass was invented in 1892 by Frank Shuman. [2] [3] Laminated glass was invented in 1903 by the French chemist Édouard Bénédictus (1878–1930). [4] These three approaches can easily be combined, allowing for the creation of glass that is at ...
Also unlike toughened glass, chemically strengthened glass may be cut after strengthening, but loses its added strength within approximately 20 mm of the cut. Similarly, when the surface of chemically strengthened glass is deeply scratched, this area loses its additional strength. Another negative of chemically strengthened glass is the added cost.
Glass fibers have a much higher tensile strength than regular glass (200-500 times stronger than regular glass). [7] This is due to the reduction of flaws in glass fibers [8] and the small cross sectional area of glass fibers, constraining maximum defect size.
The Triplex Safety Glass Company Ltd was founded in 1912 by Kent-born Reginald Delpech (30 March 1881 - 29 May 1935). [2] [3] The company was established in 1912 to build laminated windscreens in Britain, under French patents.
Float glass is a sheet of glass made by floating molten glass on a bed of molten metal of a low melting point, typically tin, [1] although lead was used for the process in the past. [2] This method gives the sheet uniform thickness and a very flat surface. [ 3 ]
In automobiles, the laminated glass panel is around 6.5 mm (0.26 inches) thick, in comparison to airplane glass being three times as thick. [21] In airliners on the front and side cockpit windows, there is often three plies of 4 mm toughened glass with 2.6 mm thick PVB between them.
Optical glass refers to a quality of glass suitable for the manufacture of optical systems such as optical lenses, prisms or mirrors.Unlike window glass or crystal, whose formula is adapted to the desired aesthetic effect, optical glass contains additives designed to modify certain optical or mechanical properties of the glass: refractive index, dispersion, transmittance, thermal expansion and ...