— "Values ranging from 21.3 to 21.5 gm/cm 3 at 20 °C have been reported for the density of annealed platinum; the best value being about 21.45 gm/cm 3 at 20 °C." 21.46 g/cm 3 — Rose, T. Kirke. The Precious Metals, Comprising Gold, Silver and Platinum .
7085 aluminum alloy is wrought type alloy. ... Properties [1] Value Density 2.85 g/cc Elements [1] Weight Percentage (%) Aluminum 87.62 - 90.42 % Chromium <= 0.04 %
The density of aluminium is 2.70 g/cm 3, about 1/3 that of steel, much lower than other commonly encountered metals, making aluminium parts easily identifiable through their lightness. [28] Aluminium's low density compared to most other metals arises from the fact that its nuclei are much lighter, while difference in the unit cell size does not ...
7093 aluminum alloy is a wrought alloy composed of aluminum, copper, magnesium, zinc ... Properties [1] Value Density 2.86 g/cc Elements [1] Percentage by weight ...
1370 Aluminium alloy is primarily aluminium ... Density: 2.70 g/cc Tensile Strength, Ultimate: 83.0 MPa Tensile Strength, Yield: 28.0 MPa Elongation at Break: 28 %
The density of precious metals could conceivably be based on Troy ounces and pounds, a possible cause of confusion. Knowing the volume of the unit cell of a crystalline material and its formula weight (in daltons), the density can be calculated. One dalton per cubic ångström is equal to a density of 1.660 539 066 60 g/cm 3.
Density 2.58 g/cc Tensile Strength, Ultimate 430 MPa Tensile Strength, Yield 330 MPa Elongation at Break 18 % Modulus of Elasticity 75.0 GPa CTE, linear 23.9 μm/m-°C @Temperature 20.0 - 100 °C Specific Heat Capacity 0.860 J/g-°C at Temperature 100 °C Thermal Conductivity 84.0 W/m-K Melting Point 560 - 670 °C Solidus 560 °C Liquidus
7255 aluminium alloy is a wrought alloy with high zinc weight percentage (from 7.8 to 8.4%). It also contains magnesium, ... Density [1] 2.86 g/cc References