Concrete is a composite material composed of aggregate bonded together with a fluid cement that cures to a solid over time. Concrete is the second-most-used substance in the world after water, [1] and is the most widely used building material. [2] Its usage worldwide, ton for ton, is twice that of steel, wood, plastics, and aluminium combined. [3]
Concrete has a very low coefficient of thermal expansion, and as it matures concrete shrinks. All concrete structures will crack to some extent, due to shrinkage and tension. Concrete which is subjected to long-duration forces is prone to creep. The density of concrete varies, but is around 2,400 kilograms per cubic metre (150 lb/cu ft). [1]
A w/c ratio higher than 0.60 is not acceptable as fresh concrete becomes "soup" [2] and leads to a higher porosity and to very poor quality hardened concrete as publicly stated by Prof. Gustave Magnel (1889-1955, Ghent University, Belgium) during an official address to American building contractors at the occasion of one of his visits in the ...
The law states the strength of a concrete mix is inversely related to the mass ratio of water to cement. [1] [2] As the water content increases, the strength of concrete decreases. Abrams’ law is a special case of a general rule formulated empirically by Feret: = / where S is the strength of concrete
Concrete is the most widely used material in existence and is behind only water as the planet's most-consumed resource. [ 2 ] Cements used in construction are usually inorganic , often lime - or calcium silicate -based, and are either hydraulic or less commonly non-hydraulic , depending on the ability of the cement to set in the presence of ...
The most common use for portland cement is in the production of concrete. [17] Concrete is a composite material consisting of aggregate (gravel and sand), cement, and water. As a construction material, concrete can be cast in almost any shape desired, and once hardened, can become a structural (load bearing) element.
AOL Mail welcomes Verizon customers to our safe and delightful email experience!
When water is added to cement, each of the compounds undergoes hydration and contributes to the final state of the concrete. [2] Only calcium silicates contribute to the strength. Tricalcium silicate is responsible for most of the early strength (first 7 days). [3] Dicalcium silicate, which reacts more slowly, only contributes to late strength.