The unit, named after Blaise Pascal, is an SI coherent derived unit defined as one newton per square metre (N/m 2). [1] It is also equivalent to 10 barye (10 Ba) in the CGS system. Common multiple units of the pascal are the hectopascal (1 hPa = 100 Pa), which is equal to one millibar , and the kilopascal (1 kPa = 1000 Pa), which is equal to ...
= in units of MPa, where HV is the Vickers hardness in N/mm 2 (or MPa) (i.e., 9.81 x numerical HV), P is the indentation load in N (typically 30 kgf is used) and T is the total crack length (mm) after application of the indenter.
If HV is first expressed in N/mm 2 (MPa), or otherwise by converting from kgf/mm 2, then the tensile strength (in MPa) of the material can be approximated as σ u ≈ HV/ c, where c is a constant determined by yield strength, Poisson's ratio, work-hardening exponent and geometrical factors – usually ranging between 2 and 4. [9]
0.8–2 MPa 120–290 psi Pressure used in boilers of steam locomotives [citation needed] 1.1 MPa 162 psi Pressure of an average human bite [citation needed] 2.8–8.3 MPa 400–1,200 psi Pressure of carbon dioxide propellant in a paintball gun [64] 5 MPa 700 psi Water pressure of the output of a coin-operated car wash spray nozzle [58] 5 MPa ...
{{convert|100|lb|kg}} → 100 pounds (45 kg) The unit-codes should be treated as case-sensitive: {{convert|100|Mm|mm}} → 100 megametres (1.0 × 10 11 mm) The output of {{convert}} can display multiple converted units, if further unit-codes are specified after the second unnamed parameter (without the pipe separator). Typical combination ...
Another Neo-Hookean linear relation between the ASTM D2240 hardness value and material elastic modulus has the form [10] =, = { < <, + < <, where is the ASTM D2240 type A hardness, is the ASTM D2240 type D hardness, and is the Young's modulus in MPa.
A four-stroke engine produces 159 N·m ... (at higher rotating speed). If the same engine is rated 72 kW at 5400 min −1 = 90 s −1, and its BMEP is 0.80 MPa, ...
The conversion in SI units is 1 ksi = 6.895 MPa, or 1 MPa = 0.145 ksi. The megapound per square inch (Mpsi) is another multiple equal to a million psi. It is used in mechanics for the elastic modulus of materials, especially for metals. [5] The conversion in SI units is 1 Mpsi = 6.895 GPa, or 1 GPa = 0.145 Mpsi.