In the recent past, HSS was commonly available in mild steel, such as A500 grade B. Today, HSS is commonly available in mild steel, A500 grade C. Other steel grades available for HSS are A847 (weathering steel), A1065 (large sections up to 50 inch sq made with SAW process), and recently approved A1085 (higher strength, tighter tolerances than ...
A36 steel has a Poisson's ratio of 0.26 and a shear modulus of 11,500 ksi (79.3 GPa). [ 7 ] A36 steel in plates, bars, and shapes with a thickness of less than 8 inches (203 millimeters) has a minimum yield strength of 36 ksi (250 MPa ) and ultimate tensile strength of 58–80 ksi (400–550 MPa).
The structural channel, C-channel or parallel flange channel (PFC), is a type of (usually structural steel) beam, used primarily in building construction and civil engineering. Its cross section consists of a wide "web", usually but not always oriented vertically, and two "flanges" at the top and bottom of the web, only sticking out on one side ...
ASTM A500 is a standard specification published by the ASTM for cold-formed welded and seamless carbon steel structural tubing in round, square, and rectangular shapes. It is commonly specified in the US for hollow structural sections, but the more stringent CSA G40.21 is preferred in Canada.
EN 10027-1 steel grade designation system. European standard steel grade names fall into two categories: [1] Steel specified by purpose of use and mechanical properties. Steel specified by chemical composition. The inclusion of a letter 'G' before the code indicates the steel is specified in the form of a casting.
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Steel never turns into a liquid below this temperature. Pure Iron ('Steel' with 0% Carbon) starts to melt at 1,492 °C (2,718 °F), and is completely liquid upon reaching 1,539 °C (2,802 °F). Steel with 2.1% Carbon by weight begins melting at 1,130 °C (2,070 °F), and is completely molten upon reaching 1,315 °C (2,399 °F).
In Canada, steel I-beams are now commonly specified using the depth and weight of the beam in metric terms. For example, a "W250x33" beam is approximately 250 millimetres (9.8 in) in depth (height of the I-beam from the outer face of one flange to the outer face of the other flange) and weighs approximately 33 kg/m (22 lb/ft; 67 lb/yd). [ 8 ]