Vickers hardness test (HV) Knoop hardness test (HK) In microindentation testing, the hardness number is based on measurements made of the indent formed in the surface of the test specimen. The hardness number is based on the applied force divided by the surface area of the indent itself, giving hardness units in kgf/mm 2. Microindentation ...
A Rockwell hardness tester. The Rockwell hardness test is a hardness test based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
The typical test uses a 10 mm (0.39 in) diameter steel ball as an indenter with a 3,000 kgf (29.42 kN; 6,614 lbf) force. For softer materials, a smaller force is used; for harder materials, a tungsten carbide ball is substituted for the steel ball. The indentation is measured and hardness calculated as:
The indentation curves have often at least thousands of data points. The hardness and elastic modulus can quickly be calculated by using a programming language or a spreadsheet. Instrumented indentation testing machines come with the software specifically designed to analyze the indentation data from their own machine.
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
Brinelling / ˈ b r ɪ n ə l ɪ ŋ / is the permanent indentation of a hard surface. It is named after the Brinell scale of hardness, in which a small ball is pushed against a hard surface at a preset level of force, and the depth and diameter of the mark indicates the Brinell hardness of the surface. Brinelling is permanent plastic ...
A nanoindenter. A nanoindenter is the main component for indentation hardness tests used in nanoindentation.Since the mid-1970s nanoindentation has become the primary method for measuring and testing very small volumes of mechanical properties.
A Berkovich tip is a type of nanoindenter tip used for testing the indentation hardness of a material. It is a three-sided pyramid which is geometrically self-similar. The popular Berkovich now has a very flat profile, with a total included angle of 142.3° and a half angle of 65.27°, measured from the axis to one of the pyramid flats.