Integral color anodizing is generally done with organic acids, but the same effect has been produced in laboratories with very dilute sulfuric acid. Integral color anodizing was originally performed with oxalic acid, but sulfonated aromatic compounds containing oxygen, particularly sulfosalicylic acid, have been more common since the 1960s. [2]
The most common conversion coating processes for metal parts with industrial use include Chromate (aluminum, steel) Phosphate (steel) Bluing (steel) Black oxide (steel) Anodizing (aluminum) Stannate (magnesium) [5] Molybdate (zinc, zinc-nickel) [6] [7] Zirconate (steel, aluminum, magnesium, galvanized steel). [1] [8] [9] Titanate (steel ...
The formula was meant to be dissolved in water at the concentration of 9.0 g/L, giving a bath with pH = 1.5. It yielded a light gold color after 1 min, and a golden-brown film after 3 min. The average thickness ranged between 200 and 1000 nm. [6] Iridite 14-2 is a chromate conversion bath for aluminum.
Black for aluminum. Boil a solution of 20 g ammonium molybdate and 5 g of sodium thiosulfate in a liter of water, immerse the objects, rinse, dry, wax or lacquer after the development of color. [31] Lustre colours. Use a solution of 280 g of sodium thiosulphate, 25 g of cupric acetate and 30 g of citric acid. It can be used on copper and its ...
For premium support please call: 800-290-4726 more ways to reach us
Photosensitive anodized aluminum was qualified to Federal Specification GG-P-455 in 1965, a document that outlines the performance of Type 1 and Type 2 photosensitive anodized aluminum. [3] Since qualification to GG-P-455, photosensitive anodized aluminum has been specified by many military, government and industrial organizations, including: