1100 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). With a minimum of 99.0% aluminium, it is the most heavily alloyed of the 1000 series. With a minimum of 99.0% aluminium, it is the most heavily alloyed of the 1000 series.
6061 sheet in the T4 condition can be formed with limited ductility in the cold state. For deep draw and complex shapes, and for the avoidance of spring-back, an aluminium hot stamping process ( Hot Form Quench ) can be used, which forms a blank at a elevated temperature (~ 550 C) in a cooled die, leaving a part in W-temper condition before ...
Aluminium is widely used in sheet metal form due to its flexibility, wide range of options, cost effectiveness, and other properties. [6] The four most common aluminium grades available as sheet metal are 1100-H14, 3003-H14, 5052-H32, and 6061-T6. [5] [7] Grade 1100-H14 is commercially pure aluminium, highly chemical and weather resistant.
Alclad is a corrosion-resistant aluminium sheet formed from high-purity aluminium surface layers metallurgically bonded (rolled onto) to high-strength aluminium alloy core material. It has a melting point of about 500 °C (932 °F).
Aluminum 1100–O (annealed) 0.20: 180 2024 aluminum alloy (heat treated—T3) 0.16: 690 5052-O 0.13 210 Aluminum 6061–O (annealed) 0.20: 205 Aluminum 6061–T6: 0.05: 410 Aluminum 7075–O (annealed) 0.17: 400 Brass, Naval (annealed) 0.49: 895 Brass 70–30 (annealed) 0.49: 900 Brass 85–15 (cold-rolled) 0.34: 580 Cobalt-base alloy (heat ...
1060 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). It is fundamentally very similar to 1050 aluminium alloy, with the difference coming down to 0.1% aluminium by weight.
6060 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is much more closely related to the alloy 6063 than to 6061.The main difference between 6060 and 6063 is that 6063 has a slightly higher magnesium content.
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.